High-Quality TPEE3362 for Optical Fiber

Type and application

Type	Product	Application and advantages
TPEE3362	Thermoplastic Polyester Elastomer TPEE	Secondary Coating Materials Used for Optical Fiber

Product description Thermoplastic polyester elastomer (TPEE) is a kind of block copolymer, It includes crystalline polyester hard segment which has properties of high melting point and high hardness and amorphous polyether or polyester soft segment which has properties of low glass transition temperature, It is formed into two phase structure, the hard segment crystallization have an effect on physical cross linking and stabilize product dimension, soft segment have an effect on amorphous polymer with high resilience.Therefore, To increase the proportion of hard section can improve the hardness, strength, heat resistance and oil resistance of TPEE. To increase the ratio of soft segments can improve the elasticity and low temperature deflection of TPEE.TPEE also has the properties of softness and elasticity of rubber, as well as the rigidity of thermoplastic and easy processing. Its shore’s hardness is 63D . Processing technology The recommended processing temperature

Zone	Extruder body 1	Extruder body 2	Extruder body 3	Extruder body 4	Extruder body 5	Flange	Extruder head	Hot water	Warm water
/℃	225	230	235	240	240	235	235	25	20

Storage and transport Package: Two package ways: 1. It is packed 900/1000KG per bag with the inner lining of aluminum foil material, outer lining of PE woven material. 2. It is packed 25KG per bag with inner lining of aluminum foil material , outer lining of kraft paper material. Transportation: The product should not be exposed to get wet or humidity during transportation, and keep it dry, clean, complete and pollution-free. Storage: The product is stored in a clean, cool, dry and ventilated warehouse away from the source of fire. If the product is found to be damped in rainy reason or with high moisture in the air, It can be used three hour later after it is dried at the temperature of 80-110℃ . Properties

Inspected properties		Test Method	Unit	Value
Rheological property	Melting Point	ISO 11357	℃	218.0±2.0
	（250℃、2160g）The melt flow rate	ISO 1133	g/10min	22
	Intrinsic viscosity	-	dL/g	1.250±0.025
Mechanical properties	Hardness after （3S）	ISO 868	Shore D	63±2
	Tensile Strength	ISO 527-1	MPa	41
	Bending Strength	-	MPa	13
	Initial Tear Resistance	ISO 34	KN`m-1	N
	Elongation at break	ISO 527-1	%	>500
	Break type	-	-	P
	Flexural Modulus	ISO 178	MPa	450
Other	Specific Gravity	ISO 1183	g/cm3	1.26
Other	Water Absorption	GB/T14190	%	0.06
Processing temperature	Drying tem.	-	℃	110
	Drying time	-	h	3
	Extruding tem.	-	℃	230-240
The data provided are the typical ranges of product properties. They should not be used to establish specification limits or used alone as the basis of design
Appearance	Supplied in cylindrical pellets free from contamination, fines and other defects.